material

Bi2MoO6

ID:

mp-555658


Tags: Dibismuth molybdenum oxide Koechlinite

Material Details

Final Magnetic Moment
0.000 μB

Calculated total magnetic moment for the unit cell within the magnetic ordering provided (see below). Typically accurate to the second digit.

Magnetic Ordering
NM
Formation Energy / Atom
-1.859 eV

Calculated formation energy from the elements normalized to per atom in the unit cell.

Energy Above Hull / Atom
0.046 eV

The energy of decomposition of this material into the set of most stable materials at this chemical composition, in eV/atom. Stability is tested against all potential chemical combinations that result in the material's composition. For example, a Co2O3 structure would be tested for decomposition against other Co2O3 structures, against Co and O2 mixtures, and against CoO and O2 mixtures.

Density
8.05 g/cm3

The calculated bulk crystalline density, typically underestimated due calculated cell volumes overestimated on average by 3% (+/- 6%)

Decomposes To
Bi2MoO6
Band Gap
0.536 eV

In general, band gaps computed with common exchange-correlation functionals such as the LDA and GGA are severely underestimated. Typically the disagreement is reported to be ~50% in the literature. Some internal testing by the Materials Project supports these statements; typically, we find that band gaps are underestimated by ~40%. We additionally find that several known insulators are predicted to be metallic.

Space Group

Hermann Mauguin
Cmce [64]
Hall
-C 2bc 2
Point Group
mmm
Crystal System
orthorhombic

Electronic Structure

Topological data for ICSD ID 37251 from Topological Materials Database
Topological Classification
trivial*
Subclassification
LCEBR
* trivial insulator or metal
Linear Combination of Elementary Band Representations

Band Structure and Density of States

Warning! Semi-local DFT tends to severely underestimate bandgaps. Please see the wiki for more info.

X-Ray Diffraction

    Select radiation source:
  • Cu
  • Ag
  • Mo
  • Fe

Calculated powder diffraction pattern; note that peak spacings may be affected due to inaccuracies in calculated cell volume, which is typically overestimated on average by 3% (+/- 6%)

X-Ray Absorption Spectra

FEFF XANES

Select an element to display a spectrum averaged over all sites of that element in the structure.

Apply Gaussian smoothing:

0 eV
3 eV
FWHM: 0 eV

Download spectra for every symmetrically equivalent absorption site in the structure.

Download FEFF Input parameters.

Warning: These results are intended to be semi-quantitative in that corrections, such as edge shifts and Debye-Waller damping, have not been included.

Substrates

Reference for minimal coincident interface area (MCIA) and elastic energy:
substrate orientation:
No elastic tensor calculated for this material, so elastic energies not avaialable. Sorting by MCIA instead.
substrate material substrate orientation film orientation MCIA [Å2]
LaAlO3 (mp-2920) <0 0 1> <0 1 0> 148.8
LaAlO3 (mp-2920) <1 0 0> <0 1 1> 290.2
LaAlO3 (mp-2920) <1 0 1> <0 1 0> 148.8
AlN (mp-661) <0 0 1> <0 1 0> 208.3
AlN (mp-661) <1 0 0> <0 1 0> 238.1
AlN (mp-661) <1 1 0> <0 1 1> 193.5
AlN (mp-661) <1 1 1> <0 1 1> 290.2
CeO2 (mp-20194) <1 0 0> <0 1 0> 29.8
CeO2 (mp-20194) <1 1 0> <1 0 1> 130.4
GaAs (mp-2534) <1 0 0> <0 1 0> 267.8
GaN (mp-804) <0 0 1> <0 1 0> 89.3
GaN (mp-804) <1 0 0> <0 1 0> 267.8
GaN (mp-804) <1 0 1> <0 1 0> 327.4
GaN (mp-804) <1 1 0> <1 0 1> 260.8
SiO2 (mp-6930) <1 0 0> <0 1 1> 193.5
SiO2 (mp-6930) <1 1 0> <0 0 1> 92.0
DyScO3 (mp-31120) <0 0 1> <0 0 1> 92.0
DyScO3 (mp-31120) <0 1 0> <0 1 0> 89.3
DyScO3 (mp-31120) <0 1 1> <0 1 0> 208.3
DyScO3 (mp-31120) <1 1 0> <1 0 0> 184.7
InAs (mp-20305) <1 0 0> <0 1 0> 148.8
ZnSe (mp-1190) <1 0 0> <0 1 0> 267.8
KTaO3 (mp-3614) <1 0 0> <0 1 0> 148.8
CdS (mp-672) <1 0 1> <0 1 0> 357.1
LiF (mp-1138) <1 0 0> <0 1 0> 148.8
Te2W (mp-22693) <0 1 1> <0 1 1> 290.2
YVO4 (mp-19133) <0 0 1> <0 1 0> 267.8
YVO4 (mp-19133) <1 1 0> <0 1 0> 327.4
Te2Mo (mp-602) <0 0 1> <0 1 0> 238.1
Ag (mp-124) <1 0 0> <0 1 0> 148.8
Bi2Te3 (mp-34202) <0 0 1> <0 1 0> 327.4
GaSe (mp-1943) <0 0 1> <0 1 0> 148.8
GaSe (mp-1943) <1 0 0> <1 1 1> 133.7
BN (mp-984) <0 0 1> <0 1 0> 148.8
BN (mp-984) <1 0 0> <0 1 0> 59.5
BN (mp-984) <1 0 1> <1 0 0> 277.0
BN (mp-984) <1 1 0> <0 1 0> 238.1
MoS2 (mp-1434) <0 0 1> <0 1 0> 89.3
MoS2 (mp-1434) <1 1 0> <0 1 0> 119.0
Al (mp-134) <1 0 0> <0 1 0> 148.8
LiGaO2 (mp-5854) <0 0 1> <0 1 1> 193.5
LiGaO2 (mp-5854) <0 1 0> <0 1 0> 327.4
LiGaO2 (mp-5854) <1 0 0> <0 1 0> 178.6
LiGaO2 (mp-5854) <1 0 1> <0 1 0> 89.3
TeO2 (mp-2125) <0 0 1> <0 1 1> 96.7
TeO2 (mp-2125) <0 1 0> <0 1 0> 267.8
TeO2 (mp-2125) <0 1 1> <0 1 0> 148.8
MoSe2 (mp-1634) <1 0 0> <1 0 1> 260.8
MoSe2 (mp-1634) <1 1 0> <1 0 1> 260.8
Ga2O3 (mp-886) <1 0 -1> <0 1 0> 148.8
Up to 50 entries displayed.
minimal coincident interface area.

Elasticity

A full elastic tensor has not been calculated for this material. Registered users can view statistical-learning-based predictions of this material's bulk and shear moduli.

Once you have registered you can also "vote" for full calculation of this material's elastic properties.

Similar Structures beta feature

Explanation of dissimilarity measure: Documentation.
material dissimilarity Ehull # of elements
Bi2TeO6 (mp-27251) 0.4249 0.000 3
Bi2MoO6 (mp-567075) 0.4334 0.044 3
Bi2SeO6 (mp-754798) 0.6219 0.097 3
Up to 5 similar elemental, binary, ternary, quaternary, etc. structures displayed (dissimilarity threshold 0.75). Ehull: energy above hull per atom [eV].

Synthesis Descriptions

All chemicals were of analytical grade and were used without further purification. In a typical synthesis, 5.0mmol of Bi(NO3)35H2O and 2.5mmol H2MoO4 were dissolved in deionized water. Then, 0.2 [...]
-Bi2Mo3O12 and -Bi2MoO6 catalysts were prepared by a co-precipitation method. A known amount of bismuth nitrate (Bi(NO3)35H2O from SigmaAldrich) was dissolved in distilled water that had been acid [...]
chef hat mixing beaker

Explore more synthesis descriptions for materials of composition Bi2MoO6.

Text computed by synthesisproject.org.

Calculation Summary

Structure Optimization

Run Type
GGA+U
Energy Cutoff
520 eV
# of K-points
None
U Values
Mo: 4.38 eV
Pseudopotentials
VASP PAW: Bi Mo_pv O
Final Energy/Atom
-6.3657 eV
Corrected Energy
-130.0721 eV
-130.0721 eV = -114.5827 eV (uncorrected energy) - 8.4275 eV (MP Anion Correction) - 7.0620 eV (MP Advanced Correction)

Detailed input parameters and outputs for all calculations


Show JSON History Show BibTex Citation Download BibTex Citation
ICSD IDs
  • 37251
Submitted by
User remarks:
  • Dibismuth molybdenum oxide
  • Koechlinite

Displaying lattice parameters for primitive cell; note that calculated cell volumes are typically overestimated on average by 3% (+/- 6%). Note the primitive cell may appear less symmetric than the conventional cell representation (see "Structure Type" selector below the 3d structure)