Final Magnetic Moment0.001 μBCalculated total magnetic moment for the unit cell within the magnetic ordering provided (see below). Typically accurate to the second digit. |
Magnetic OrderingNM |
Formation Energy / Atom0.043 eVCalculated formation energy from the elements normalized to per atom in the unit cell. |
Energy Above Hull / Atom0.360 eVThe energy of decomposition of this material into the set of most stable materials at this chemical composition, in eV/atom. Stability is tested against all potential chemical combinations that result in the material's composition. For example, a Co2O3 structure would be tested for decomposition against other Co2O3 structures, against Co and O2 mixtures, and against CoO and O2 mixtures. |
Density5.07 g/cm3The calculated bulk crystalline density, typically underestimated due calculated cell volumes overestimated on average by 3% (+/- 6%) |
Decomposes ToY2C + Y4C5 |
Band Gap0.000 eVIn general, band gaps computed with common exchange-correlation functionals such as the LDA and GGA are severely underestimated. Typically the disagreement is reported to be ~50% in the literature. Some internal testing by the Materials Project supports these statements; typically, we find that band gaps are underestimated by ~40%. We additionally find that several known insulators are predicted to be metallic. |
Hermann MauguinFm3m [225] |
Hall-F 4 2 3 |
Point Groupm3m |
Crystal Systemcubic |
Calculated powder diffraction pattern; note that peak spacings may be affected due to inaccuracies in calculated cell volume, which is typically overestimated on average by 3% (+/- 6%)
Select an element to display a spectrum averaged over all sites of that element in the structure.
Apply Gaussian smoothing:
Download spectra for every symmetrically equivalent absorption site in the structure.
Download FEFF Input parameters.
substrate material | substrate orientation | film orientation | MCIA† [Å2] |
---|---|---|---|
BaF2 (mp-1029) | <1 0 0> | <1 0 0> | 207.6 |
BaF2 (mp-1029) | <1 1 0> | <1 1 0> | 110.1 |
GaN (mp-804) | <0 0 1> | <1 0 0> | 207.6 |
GaN (mp-804) | <1 0 0> | <1 0 0> | 129.7 |
GaN (mp-804) | <1 0 1> | <1 0 0> | 285.4 |
GaN (mp-804) | <1 1 0> | <1 0 0> | 233.5 |
GaN (mp-804) | <1 1 1> | <1 1 1> | 314.6 |
SiO2 (mp-6930) | <0 0 1> | <1 0 0> | 129.7 |
SiO2 (mp-6930) | <1 0 0> | <1 1 0> | 110.1 |
SiO2 (mp-6930) | <1 0 1> | <1 0 0> | 285.4 |
SiO2 (mp-6930) | <1 1 1> | <1 1 0> | 110.1 |
KCl (mp-23193) | <1 0 0> | <1 0 0> | 207.6 |
KCl (mp-23193) | <1 1 0> | <1 1 0> | 110.1 |
DyScO3 (mp-31120) | <0 0 1> | <1 1 0> | 293.6 |
DyScO3 (mp-31120) | <1 1 0> | <1 0 0> | 129.7 |
InAs (mp-20305) | <1 0 0> | <1 1 1> | 224.7 |
InAs (mp-20305) | <1 1 0> | <1 1 0> | 110.1 |
ZnSe (mp-1190) | <1 0 0> | <1 0 0> | 129.7 |
ZnSe (mp-1190) | <1 1 0> | <1 1 0> | 146.8 |
ZnSe (mp-1190) | <1 1 1> | <1 1 1> | 179.8 |
KTaO3 (mp-3614) | <1 0 0> | <1 0 0> | 129.7 |
CdS (mp-672) | <0 0 1> | <1 1 1> | 44.9 |
CdS (mp-672) | <1 0 0> | <1 1 0> | 256.9 |
CdS (mp-672) | <1 0 1> | <1 1 0> | 330.3 |
CdS (mp-672) | <1 1 0> | <1 1 0> | 146.8 |
LiF (mp-1138) | <1 0 0> | <1 0 0> | 129.7 |
LiF (mp-1138) | <1 1 0> | <1 1 0> | 73.4 |
LiF (mp-1138) | <1 1 1> | <1 1 0> | 146.8 |
Te2W (mp-22693) | <0 0 1> | <1 0 0> | 181.6 |
Te2W (mp-22693) | <0 1 0> | <1 1 0> | 110.1 |
Te2W (mp-22693) | <0 1 1> | <1 0 0> | 233.5 |
Te2W (mp-22693) | <1 1 0> | <1 1 0> | 110.1 |
Te2W (mp-22693) | <1 1 1> | <1 1 1> | 224.7 |
YVO4 (mp-19133) | <0 0 1> | <1 0 0> | 51.9 |
YVO4 (mp-19133) | <1 0 0> | <1 1 0> | 183.5 |
YVO4 (mp-19133) | <1 0 1> | <1 0 0> | 207.6 |
TePb (mp-19717) | <1 0 0> | <1 0 0> | 207.6 |
TePb (mp-19717) | <1 1 1> | <1 1 1> | 314.6 |
Te2Mo (mp-602) | <0 0 1> | <1 0 0> | 129.7 |
Te2Mo (mp-602) | <1 0 0> | <1 1 0> | 110.1 |
Te2Mo (mp-602) | <1 0 1> | <1 1 1> | 224.7 |
Ag (mp-124) | <1 0 0> | <1 0 0> | 233.5 |
Ag (mp-124) | <1 1 0> | <1 1 0> | 73.4 |
Ag (mp-124) | <1 1 1> | <1 1 0> | 146.8 |
Bi2Te3 (mp-34202) | <0 0 1> | <1 1 0> | 330.3 |
GaSe (mp-1943) | <0 0 1> | <1 1 0> | 256.9 |
BN (mp-984) | <0 0 1> | <1 1 0> | 110.1 |
BN (mp-984) | <1 0 0> | <1 0 0> | 77.8 |
BN (mp-984) | <1 0 1> | <1 0 0> | 259.5 |
BN (mp-984) | <1 1 0> | <1 1 0> | 330.3 |
Stiffness Tensor Cij (GPa) |
|||||
---|---|---|---|---|---|
262 | 94 | 94 | 0 | 0 | 0 |
94 | 262 | 94 | 0 | 0 | 0 |
94 | 94 | 262 | 0 | 0 | 0 |
0 | 0 | 0 | 61 | 0 | 0 |
0 | 0 | 0 | 0 | 61 | 0 |
0 | 0 | 0 | 0 | 0 | 61 |
Compliance Tensor Sij (10-12Pa-1) |
|||||
---|---|---|---|---|---|
4.7 | -1.2 | -1.2 | 0 | 0 | 0 |
-1.2 | 4.7 | -1.2 | 0 | 0 | 0 |
-1.2 | -1.2 | 4.7 | 0 | 0 | 0 |
0 | 0 | 0 | 16.3 | 0 | 0 |
0 | 0 | 0 | 0 | 16.3 | 0 |
0 | 0 | 0 | 0 | 0 | 16.3 |
Shear Modulus GV70 GPa |
Bulk Modulus KV150 GPa |
Shear Modulus GR69 GPa |
Bulk Modulus KR150 GPa |
Shear Modulus GVRH69 GPa |
Bulk Modulus KVRH150 GPa |
Elastic Anisotropy0.12 |
Poisson's Ratio0.30 |
material | dissimilarity | Ehull | # of elements |
---|---|---|---|
Sr4SO3 (mp-1079788) | 0.0000 | 0.200 | 3 |
BaSr3O4 (mp-984729) | 0.0000 | 0.044 | 3 |
ScH4Pd3 (mp-981386) | 0.0000 | 0.037 | 3 |
Sr3CdO4 (mp-981103) | 0.0000 | 0.019 | 3 |
SrCa3O4 (mp-978844) | 0.0000 | 0.040 | 3 |
TiH (mp-1060435) | 0.0000 | 0.045 | 2 |
USe (mp-911057) | 0.0000 | 0.000 | 2 |
TcC (mp-1009876) | 0.0000 | 0.650 | 2 |
TcC (mp-1009837) | 0.0000 | 0.650 | 2 |
MgCd (mp-1039157) | 0.0000 | 0.249 | 2 |
Sc (mp-1008681) | 0.0000 | 0.719 | 1 |
Ca (mp-10683) | 0.0000 | 0.400 | 1 |
C (mp-998866) | 0.0000 | 2.755 | 1 |
Sb (mp-133) | 0.0000 | 0.051 | 1 |
Na (mp-1093989) | 0.0000 | 1.076 | 1 |
Run TypeGGA |
Energy Cutoff520 eV |
# of K-pointsNone |
U Values-- |
PseudopotentialsVASP PAW: Y_sv C |
Final Energy/Atom-7.8032 eV |
Corrected Energy-15.6063 eV
-15.6063 eV = -15.6063 eV (uncorrected energy)
|
Displaying lattice parameters for primitive cell; note that calculated cell volumes are typically overestimated on average by 3% (+/- 6%). Note the primitive cell may appear less symmetric than the conventional cell representation (see "Structure Type" selector below the 3d structure)